Deformation, failure and removal mechanisms of thin film structures in abrasive machining
Received date: 2016-08-31
Revised date: 2016-12-19
Online published: 2017-03-25
Thin film structures are becoming increasingly more important for industrial applications such as the making of solar panels, microelectronic devices and micro systems. However, the challenges encountered in the machining of thin film structures have been a bottleneck that impedes further wide spread uses of such structures. The development of material removal processes that are capable of producing a damage free surface at high removal rates is critical for cost effective production. Such development relies highly on a comprehensive understanding of the deformation, failure and removal mechanisms of thin film structures involved in mechanical loading. In this paper, the current understanding of the deformation characteristics of thin film systems was reviewed to provide important insights into the interfacial failure under mechanical loading, with focuses on the interfacial failure mechanisms and existing problems in the machining of thin film structures. The key characterization techniques were outlined. In particular, the recent progress in the abrasive machining of a thin film multilayer structure was summarized. The potential research directions were also presented in the end of the review.
Key words： Abrasive machining; Thin film; Bilayer; Multilayer; Interface; Deformation; Failure
Cheng-Wei Kang , Han Huang . Deformation, failure and removal mechanisms of thin film structures in abrasive machining[J]. Advances in Manufacturing, 2017 , 5(1) : 1 -19 . DOI: 10.1007/s40436-016-0165-2
1. Bhusan B (2003) Springer handbook of nanotechnology. Springer, New York
2. Chen Y, McIntyre PC (2007) Lead zirconate titanate ferroelectric thin film capacitors:effects of surface treatments on ferroelectric properties. Appl Phys Lett 91:072910
3. Jayaraman V, Lin Y, Pakala M et al (1995) Fabrication of ultrathin metallic membranes on ceramic supports by sputter deposition. J Membr Sci 99:89-100
4. Kim SS, Kim ST, Ahn JM et al (2004) Magnetic and microwave absorbing properties of Co-Fe thin films plated on hollow ceramic microspheres of low density. J Magn Magn Mater 271:39-45
5. Bowden N, Brittain S, Evans AG et al (1998) Spontaneous formation of ordered structures in thin films of metals supported on an elastomeric polymer. Nature 393:146-149
6. Schmitt J, Decher G, Dressick WJ et al (1997) Metal nanoparticle/polymer superlattice films:fabrication and control of layer structure. Adv Mater 9:61-65
7. Bouclé J, Ravirajanac P, Nelson J (2007) Hybrid polymer-metal oxide thin films for photovoltaic applications. J Mater Chem 17:3141-3153
8. Ajayan PM, Schadler LS, Braun PV (2006) Nanocomposite science and technology. Wiley, New York
9. Giannelis EP (1996) Polymer layered silicate nanocomposites. Adv Mater 8:29-35
10. Favache A, Sacre CH, Coulombier M et al (2015) Fracture mechanics based analysis of the scratch resistance of thin brittle coatings on a soft interlayer. Wear 330:461-468
11. Wang J, Neaton J, Zheng H et al (2003) Epitaxial BiFeO3 multiferroic thin film heterostructures. Science 299:1719-1722
12. Pang SC, Anderson MA, Chapman TW (2000) Novel electrode materials for thin-film ultracapacitors:comparison of electrochemical properties of sol-gel-derived and electrodeposited manganese dioxide. J Electrochem Soc 147:444-450
13. Sumitomo T, Huang H, Zhou L (2011) Deformation and material removal in a nanoscale multi-layer thin film solar panel using nanoscratch. Int J Mach Tools Manuf 51:182-189
14. Sumitomo T, Huang H, Zhou L et al (2011) Nanogrinding of multi-layered thin film amorphous Si solar panels. Int J Mach Tools Manuf 51:797-805
15. Kim KS, Kim J (1988) Elasto-plastic analysis of the peel test for thin film adhesion. J Eng Mater Technol 110:266-273
16. Hegemann D, Brunner H, Oehr C (2003) Plasma treatment of polymers for surface and adhesion improvement. Nucl Instrum Methods Phys Res Sect B 208:281-286
17. Kohl JG, Singer IL (1999) Pull-off behavior of epoxy bonded to silicone duplex coatings. Prog Org Coat 36:15-20
18. Ma Q (1997) A four-point bending technique for studying subcritical crack growth in thin films and at interfaces. J Mater Res 12:840-845
19. Dayal P, Savvides N, Hoffman M (2009) Characterisation of nanolayered aluminium/palladium thin films using nanoindentation. Thin Solid Films 517:3698-3703
20. Pharr G, Oliver W (1992) Measurement of thin-film mechanicalproperties using nanoindentation. MRS Bull 17:28-33
21. Navamathavan R, Kim KK, Hwang DK et al (2006) A nanoindentation study of the mechanical properties of ZnO thin films on (0001) sapphire. Appl Surf Sci 253:464-467
22. Fang TH, Chang WJ, Lin CM (2005) Nanoindentation and nanoscratch characteristics of Si and GaAs. Microelectron Eng 77:389-398
23. Wu Y, Huang H, Zou J et al (2010) Nanoscratch-induced phase transformation of monocrystalline Si. Scripta Mater 63:847-850
24. Wu Y, Huang H, Zou J et al (2009) Nanoscratch-induced deformation of single crystal silicon. J Vac Sci Technol B 27:1374-1377
25. Chang SY, Tsai HC, Chang JY et al (2008) Analyses of interface adhesion between porous SiOCH low-k film and SiCN layers by nanoindentation and nanoscratch tests. Thin Solid Films 516:5334-5338
26. Kang C, Huang H (2016) Mechanical load-induced interfacial failure of a thin film multilayer in nanoscratching and diamond lapping. J Mater Process Technol 229:528-540
27. Lu M, Xie H, Huang H et al (2013) Indentation-induced delamination of plasma-enhanced chemical vapor deposition silicon nitride film on gallium arsenide substrate. J Mater Res 28:1047-1055
28. Roy S, Darque-Ceretti E, Felder E et al (2010) Experimental analysis and finite element modelling of nano-scratch test applied on 40-120 nm SiCN thin films deposited on Cu/Si substrate. Thin Solid Films 518:3859-3865
29. Rao SS (2010) The finite element method in engineering. Elsevier, Amsterdam
30. Torres-Torres D, Munoz-Saldana J, Gutierrez-Ladron-de Guevara L et al (2010) Geometry and bluntness tip effects on elastic-plastic behaviour during nanoindentation of fused silica:experimental and FE simulation. Model Simul Mater Sci Eng 18:1825-1830
31. Lee KM, Yeo CD, Polycarpou AA (2008) Relationship between scratch hardness and yield strength of elastic perfectly plastic materials using finite element analysis. J Mater Res 23:2229-2237
32. Lu M, Huang H (2014) Determination of the energy release rate in the interfacial delamination of silicon nitride film on gallium arsenide substrate via nanoindentation. J Mater Res 29:801-810
33. Evans A, Drory M, Hu M (1988) The cracking and decohesion of thin films. J Mater Res 3:1043-1049
34. Fischer-Cripps AC (2006) Critical review of analysis and interpretation of nanoindentation test data. Surf Coat Technol 200:4153-4165
35. Oliver WC, Pharr GM (1992) Improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res 7:1564-1583
36. Gerberich W, Yu W, Kramer D et al (1998) Elastic loading and elastoplastic unloading from nanometer level indentations for modulus determinations. J Mater Res 13:421-439
37. Taylor CA, Wayne MF, Chiu WK (2003) Residual stress measurement in thin carbon films by Raman spectroscopy and nanoindentation. Thin Solid Films 429:190-200
38. Marshall D, Evans A (1984) Measurement of adherence of residually stressed thin films by indentation. I. Mechanics of interface delamination. J Appl Phys 56:2632-2638
39. Kriese MD, Gerberich WW, Moody NR (1999) Quantitative adhesion measures of multilayer films:part I. Indentation mechanics. J Mater Res 14:3007-3018
40. Chen J, Bull S (2007) Indentation fracture and toughness assessment for thin optical coatings on glass. J Phys D Appl Phys 40:5401-5407
41. Chen J, Bull S (2010) Approaches to investigate delamination and interfacial toughness in coated systems:an overview. J Phys D Appl Phys 44:369-379
42. Volinsky A, Moody N, Gerberich W (2002) Interfacial toughness measurements for thin films on substrates. Acta Mater 50:441-466
43. Burnett PJ, Rickerby D (1987) The mechanical properties of wear-resistant coatings:I:modelling of hardness behaviour. Thin Solid Films 148:41-50
44. Li X, Bhushan B (1998) Measurement of fracture toughness of ultra-thin amorphous carbon films. Thin Solid Films 315:214-221
45. Chen J, Bull S (2009) Finite element analysis of contact induced adhesion failure in multilayer coatings with weak interfaces. Thin Solid Films 517:3704-3711
46. Lu M, Huang H (2015) Interfacial adhesion of film/substrate system characterized by nanoindentation. In:Thin films and coatings:toughening and toughness characterization. CRC Press, pp 315-376
47. Hudson JA, Harrison JP (2000) Engineering rock mechanics-an introduction to the principles. Elsevier, Amsterdam
48. Abdul-Baqi A, Van der Giessen E (2001) Delamination of a strong film from a ductile substrate during indentation unloading. J Mater Res 16:1396-1407
49. Li X, Bhushan B (1999) Micro/nanomechanical and tribological characterization of ultrathin amorphous carbon coatings. J Mater Res 14:2328-2337
50. Zhang S, Sun D, Fu Y et al (2005) Toughness measurement of thin films:a critical review. Surf Coat Technol 198:74-84
51. Li X, Diao D, Bhushan B (1997) Fracture mechanisms of thin amorphous carbon films in nanoindentation. Acta Mater 45:4453-4461
52. Liao C, Guo D, Wen S et al (2014) The assessment of interface adhesion of Cu/Ta/Black DiamondTM/Si films stack structure by nanoindentation and nanoscratch tests. Tribol Lett 53:401-410
53. Zhao X, Xie Z, Munroe P (2011) Nanoindentation of hard multilayer coatings:finite element modelling. Mater Sci Eng A 528:1111-1116
54. Lackner J, Major L, Kot M (2011) Microscale interpretation of tribological phenomena in Ti/TiN soft-hard multilayer coatings on soft austenite steel substrates. Bull Pol Acad Sci Tech Sci 59:343-355
55. Sanchez J, El-Mansy S, Sun B et al (1999) Cross-sectional nanoindentation:a new technique for thin film interfacial adhesion characterization. Acta Mater 47:4405-4413
56. Elizalde M, Sanchez J, Martinez-Esnaola J et al (2003) Interfacial fracture induced by cross-sectional nanoindentation in metal-ceramic thin film structures. Acta Mater 51:4295-4305
57. Ocaña I, Molina-Aldareguia J, Gonzalez D et al (2006) Fracture characterization in patterned thin films by cross-sectional nanoindentation. Acta Mater 54:3453-3462
58. Scherban T, Pantuso D, Sun B et al (2003) Characterization of interconnect interfacial adhesion by cross-sectional nanoindentation. Int J Fract 120:421-429
59. Heavens O (1950) Some factors influencing the adhesion of films produced by vacuum evaporation. J Phys Radium 11:355-360
60. Deng H, Scharf TW, Barnard JA (1997) Adhesion assessment of silicon carbide, carbon, and carbon nitride ultrathin overcoats by nanoscratch techniques. J Appl Phys 81:5396-5398
61. Wei C, Yen JY (2007) Effect of film thickness and interlayer on the adhesion strength of diamond like carbon films on different substrates. Diam Relat Mater 16:1325-1330
62. Beake B, Harris A, Liskiewicz T (2013) Review of recent progress in nanoscratch testing. Tribol Mater Surf Interfaces 7:87-96
63. Gassilloud R, Ballif C, Gasser P et al (2005) Deformation mechanisms of silicon during nanoscratching. Phys Status Solidi 202:2858-2869
64. Bakshi SR, Keshri AK, Agarwal A (2011) A comparison of mechanical and wear properties of plasma sprayed carbon nanotube reinforced aluminum composites at nano and macro scale. Mater Sci Eng A 528:3375-3384
65. Lian D (2010) Effect of annealing on the nanoscratch behavior of multilayer Si0.8 Ge0.2/Si films. Appl Surf Sci 257:911-916
66. Sun H, Irwan R, Huang H et al (2010) Surface characteristics and removal mechanism of cemented tungsten carbides in nanoscratching. Wear 268:1400-1408
67. Larsson M, Olsson M, Hedenqvist P et al (2000) Mechanisms of coating failure as demonstrated by scratch and indentation testing of TiN coated HSS. Surf Eng 16:436-444
68. Steinmann P, Tardy Y, Hintermann H (1987) Adhesion testing by the scratch test method:the influence of intrinsic and extrinsic parameters on the critical load. Thin Solid Films 154:333-349
69. Bellido-Gonzalez V, Stefanopoulos N, Deguilhen F (1995) Friction monitored scratch adhesion testing. Surf Coat Technol 74:884-889
70. Beuth J (1992) Cracking of thin bonded films in residual tension. Int J Solids Struct 29:1657-1675
71. Ramsey P, Chandler H, Page T (1991) Bending tests to estimate the through-thickness strength and interfacial shear strength in coated systems. Thin Solid Films 201:81-89
72. Von Stebut J, Lapostolle F, Bucsa M et al (1999) Acoustic emission monitoring of single cracking events and associated damage mechanism analysis in indentation and scratch testing. Surf Coat Technol 116:160-171
73. Tang W, Weng X, Deng L et al (2007) Nano-scratch experiments of Au/NiCr multi-layered films for microwave integrated circuits. Surf Coat Technol 201:5664-5666
74. Beake B, Davies M, Liskiewicz T et al (2013) Nano-scratch, nanoindentation and fretting tests of 5-80 nm Ta-C films on Si (100). Wear 301:575-582
75. Beake B, Ogwu A, Wagner T (2006) Influence of experimental factors and film thickness on the measured critical load in the nanoscratch test. Mater Sci Eng A 423:70-73
76. Shi B, Sullivan JL, Beake BD (2008) An investigation into which factors control the nanotribological behaviour of thin sputtered carbon films. J Phys D Appl Phys 41:045303
77. Li J, Beres W (2006) Three-dimensional finite element modelling of the scratch test for a TiN coated titanium alloy substrate. Wear 260:1232-1242
78. Holmberg K, Laukkanen A, Ronkainen H et al (2003) A model for stresses, crack generation and fracture toughness calculation in scratched TiN-coated steel surfaces. Wear 254:278-291
79. Kitamura T, Hirakata H, Itsuji T (2003) Effect of residual stress on delamination from interface edge between nano-films. Eng Fract Mech 70:2089-2101
80. Van Der Laan D, Ekin J, Clickner C et al (2007) Delamination strength of YBCO coated conductors under transverse tensile stress. Supercond Sci Technol 20:765-770
81. Sumitomo T, Huang H, Zhou L (2011) Multi-scale deformation and material removal in amorphous Si thin film solar panels. Int J Nanomanuf 7:39-53
82. Zhang C, Ohmori H, Marinescu I et al (2001) Grinding of ceramic coatings with cast iron bond diamond wheel. A comparative study:ELID and rotary dressers. Int J Adv Manuf Technol 18:545-552
83. Murthy J, Rao D, Venkataraman B (2001) Effect of grinding on the erosion behaviour of a WC-Co-Cr coating deposited by HVOF and detonation gun spray processes. Wear 249:592-600
84. Massad RB (1984) Diamond wheel grinding of thermal spray materials. Therm Spray Coat 139-146
85. Stephenson D, Hedge J, Corbett J (2002) Surface finishing of Ni-Cr-B-Si composite coatings by precision grinding. Int J Mach Tools Manuf 42:357-363
86. Liu X, Zhang B (2002) Effects of grinding process on residual stresses in nanostructured ceramic coatings. J Mater Sci 37:3229-3239
87. Zhang B, Liu X, Brown C et al (2002) Microgrinding of nanostructured material coatings. CIRP Ann Manuf Technol 51:251-254
88. Liu X, Zhang B (2003) Grinding of nanostructural ceramic coatings:damage evaluation. Int J Mach Tools Manuf 43:161-167
89. Liu X, Zhang B, Deng Z (2002) Grinding of nanostructured ceramic coatings:surface observations and material removal mechanisms. Int J Mach Tools Manuf 42:1665-1676
90. Bifano TG, Dow TA, Scattergood RO (1991) Ductile-regime grinding:a new technology for machining brittle materials. J Eng Ind 113:184-189
91. Huang H, Liu Y (2003) Experimental investigations of machining characteristics and removal mechanisms of advanced ceramics in high speed deep grinding. Int J Mach Tools Manuf 43:811-823
92. Jackson M, Davis C, Hitchiner M et al (2001) High-speed grinding with CBN grinding wheels-applications and future technology. J Mater Process Technol 110:78-88
93. Kang CW, Huang H. A comparative study of conventional and high speed grinding characteristics of a thin film multilayer structure. Precis Eng
94. Needleman A (1972) A numerical study of necking in circular cylindrical bar. J Mech Phys Solids 20:111-127
95. Needleman A (1987) A continuum model for void nucleation by inclusion debonding. J Appl Mech 54:525-531
/
| 〈 |
|
〉 |