To predict the microstructure evolution and reveal the forming mechanism of Ni-based superalloy cylindrical parts during hot power spinning, a finite element method (FEM) model of deformation-heat transfermicrostructure evolution was established using MSC.Marc software. A numerical simulation was then conducted based on the secondary development of user subroutines, to investigate evolution of the microstructure of a Haynes 230 alloy cylindrical part during hot power spinning. The volume fraction of dynamic recrystallization (DRX) and the grain size of Haynes 230 alloy cylindrical parts during hot power spinning were analyzed. The results showed that the DRX of the spun workpiece was more obvious with an increase in the forming temperature, T, and the total thinning ratio of wall thickness, Ψt. Furthermore, the complete DRX microstructure with fine and uniform grains was obtained when T ≥ 1 100℃ and Ψt ≥ 56%, but the grain size of the spun workpiece decreased slightly with an increase in the roller feed rate, f. The experimental results conformed well with simulation results.
The full text can be downloaded at https://link.springer.com/content/pdf/10.1007%2Fs40436-018-0242-9.pdf
Qin-Xiang Xia
,
Jin-Chuan Long
,
Ning-Yuan Zhu
,
Gang-Feng Xiao
. Research on the microstructure evolution of Ni-based superalloy cylindrical parts during hot power spinning[J]. Advances in Manufacturing, 2019
, 7(1)
: 52
-63
.
DOI: 10.1007/s40436-018-0242-9
1. Lin YC, Wen DX, Deng J et al (2014) Constitutive models for high-temperature flow behaviors of a Ni-based superalloy. Mater Des 59(9):115-123
2. Xia QX, Zhu NY, Cheng XQ et al (2017) The classification and a review of hot power spinning of difficult-to-deform metals. Int J Mater Prod Technol 54(1-3):212-235
3. Xia QX, Huang Y, Cheng XQ et al (2015) Development of constitutive model of Haynes230 at high temperature based on Johnson-Cook model. In:Proceedings of 34th international deep drawing research group, Shanghai, China
4. Xia QX, Xiao GF, Long H et al (2014) A review of process advancement of novel metal spinning. Int J Mach Tools Manuf 85:100-121
5. Fazeli AR, Ghoreishi M (2009) Investigation of effective parameters on surface roughness in thermomechanical tube spinning process. Int J Mater Form 2(4):261-270
6. Velay V, Matsumoto H et al (2016) Behavior modeling and microstructural evolutions of Ti-6Al-4V alloy under hot forming conditions. Int J Mech Sci 108:1-13
7. Wang XK, Xia QX, Cheng XQ (2017) Deformation behavior of Haynes230 superalloy during backward flow forming. Int J Precis Eng Manuf 18(1):77-83
8. Wang XK, Xia QX, Cheng XQ et al (2017) A study on nonuniform deformation of backward flow forming and its influencing factors. Int J Adv Manuf Technol 93(9-12):4143-4152
9. Zhao GY, Lu CJ, Zhang RY et al (2016) Uneven plastic deformation behavior of high-strength cast aluminum alloy tube in multi-pass hot power backward spinning. Int J Adv Manuf Technol 88(1-4):907-921
10. Sun LL, Kou HC, Hu R et al (2010) FEM numerical simulation of first-pass heat spinning for Ni-Cr-W-Mo superalloy workpiece with curvilinear shape. J Plastic Eng 17(2):33-38
11. Chen Y, Xu WC, Shan DB et al (2011) Microstructure evolution of TA15 titanium alloy during hot power spinning. Trans Nonferrous Met Soc China 21:323-327
12. Rentsch B, Manopulo N, Hora P (2017) Numerical modelling, validation and analysis of multi-pass sheet metal spinning processes. Int J Mater Form 10(4):641-651
13. Liu YX, Lin YC, Li HB et al (2015) Study of dynamic recrystallization in a Ni-based superalloy by experiments and cellular automaton model. Mater Sci Eng A 626:432-440
14. Marandi A, Zarei-Hanzaki R, Zarei-Hanzaki A et al (2014) Dynamic recrystallization behavior of new transformation-twinning induced plasticity steel. Mater Sci Eng A 607:397-408
15. Lin YC, Chen XM (2011) A critical review of experimental results and constitutive descriptions for metals and alloys in hot working. Mater Des 32(4):1733-1759
16. Li YS, Zhang Y, Tao NR et al (2009) Effect of the Zener-Hollomon parameter on the microstructures and mechanical properties of Cu subjected to plastic deformation. Acta Mater 57(3):761-772
17. Xiao GF, Zhu NY, Long JC et al (2018) Research on precise control of microstructure and mechanical properties of Ni-based superalloy cylindrical parts during hot backward flow spinning. J Manuf Processes 34:140-147
18. Zhu NY, Xia QX, Cheng XQ (2017) Dynamic recrystallization microstructure evolution of Haynes230 alloy based on cellular automata. J Cent South Univ (Sci Technol) 48(9):2316-2323
19. Wang CH, Liu KZ, Zhou L (2017) Spinning technology. Fujian Science and Technology Press, China
20. Zhang Q, Fan SQ, Zhao SD et al (2010) Numerical simulation research on a new spinning process:double-roller clamping spinning process. Int J Mater Form 3(1):121-125
21. Xia QX (2017) Novel spinning forming technology. Science Press, China
22. Music O, Allwood JM, Kawai K (2010) A review of the mechanics of metal spinning. J Mater Process Technol 210(1):3-23
23. Balasundar I, Raghu T (2010) Effect of friction model in numerical analysis of equal channel angular pressing process. Mater Des 31(1):449-457
24. Aghasafari P, Salimi M, Daraei A (2014) Flow stress evaluation in hot rolling of steel. J Mater Eng Perform 23:2819-2828
25. Zhen M, Yang H, Guo J et al (2015) Review on hot spinning for difficult-to-deform lightweight metals. Trans Nonferrous Met Soc China 25(6):1732-1743
26. HAYNES 230 Alloy. High temperature alloys brochure (2009) Haynes International, Inc
27. Xiao GF, Xia QX, Cheng XQ et al (2015) Research on the grain refinement method of cylindrical parts by power spinning. Int J Adv Manuf Technol 78(5-8):971-979