Vertical centrifugal casting can significantly enhance the filling capability of molten metals, enabling the production of complex thin-walled castings at near-rapid cooling rates. In this study, the melt flow, solidification structures, and defects in 316 L steel cast strips with a geometry of 80 mm×60 mm×2.5 mm produced by vertical centrifugal casting were numerically and experimentally analyzed under different rotation speeds. With gradually increasing the rotation speed from 150 r/min to 900 r/min, the simulated results showed the shortest filling time and minimum porosity volume in the cast strip at a rotation speed of 600 r/min. Since a strong turbulent flow was generated by the rotation of the mold cavity during the filling process, experimental results showed that a “non-dendritic” structure was obtained in 316 L cast strip when centrifugal force was involved, whereas the typical dendritic structure was observed in the reference sample without rotation. Most areas of the cast strip exhibited one-dimensional cooling, but three-sided cooling appeared near the side of the cast strip. Moreover, the pores and cracks in the 316 L strips were detected by computed tomography scanning and analyzed with the corresponding numerical simulations. Results indicated the existence of an optimal rotational speed for producing cast strips with minimal casting defects. This study provides a better understanding of the filling and solidification processes of strips produced by vertical centrifugal casting.
The full text can be downloaded at https://link.springer.com/article/10.1007/s40436-023-00439-z
Li-Bing Liu
,
Cong-Hui Hu
,
Yun-Hu Zhang
,
Chang-Jiang Song
,
Qi-Jie Zhai
. Melt flow, solidification structures, and defects in 316 L steel strips produced by vertical centrifugal casting[J]. Advances in Manufacturing, 2023
, 11(4)
: 636
-646
.
DOI: 10.1007/s40436-023-00439-z
1 Williams SE, Akhil SK, Inambao FL (2016) Centrifugal casting technique baseline knowledge, applications, and processing parameters: overview. Int J Mater Res 107:960-969
2 Humphreys NJ, McBride D, Shevchenko DM et al (2013) Modelling and validation: casting of Al and TiAl alloys in gravity and centrifugal casting processes. Appl Math Model 37:7633-7643
3 Yang L, Chai LH, Liang YF et al (2015) Numerical simulation and experimental verification of gravity and centrifugal investment casting low pressure turbine blades for high Nb-TiAl alloy. Intermetallics 66:149-155
4 Xu DM, Jia LM, Fu HZ (2008) Effects of centrifugal and Coriolis forces on the mold-filling behavior of titanium melts in vertically rotating molds. China Foundry 5:249-257
5 Shailesh RA, Tattimani MS, Rao SS (2015) Understanding melt flow behavior for Al-Si alloys processed through vertical centrifugal casting. Mater Manuf Process 30:1305-1311
6 Lu SL, Xiao FR, Zhang SJ et al (2014) Simulation study on the centrifugal casting wet-type cylinder liner based on ProCAST. Appl Therm Eng 73:512-521
7 McBride D, Humphreys NJ, Croft TN et al (2013) Complex free surface flows in centrifugal casting: computational modelling and validation experiments. Comput Fluids 82:63-72
8 Li CY, Wu SP, Guo JJ et al (2008) Castability of thin walled titanium alloy castings in vertical centrifugal field. Mater Sci Technol 24:1209-1213
9 Chang SR, Kim JM, Hong CP (2001) Numerical simulation of microstructure evolution of Al alloys in centrifugal casting. ISIJ Int 41:738-747
10 Zhang J, Jiang Y, Zheng W et al (2021) Revisiting the formation mechanism of intragranular κ-carbide in austenite of a Fe-Mn-Al-Cr-C low-density steel. Scr Mater 199:113836. https://doi.org/10.1016/j.scriptamat.2021.113836
11 Liu Y, Liu M, Zhang J et al (2021) Microstructure and mechanical properties of a Fe-28Mn-9Al-1.2C-(0, 3, 6, 9)Cr austenitic low-density steel. Mat Sci Eng A 821:141583. https://doi.org/10.1016/j.msea.2021.141583
12 Chen Z, Liu MX, Zhang JK et al (2021) Effect of annealing treatment on microstructures and properties of austenite-based Fe-28Mn-9Al-0.8C lightweight steel with addition of Cu. China Foundry 18:207-216
13 Zhang J, Hu C, Zhang Y et al (2020) Microstructures, mechanical properties and deformation of near-rapidly solidified low-density Fe-20Mn-9Al-1.2C-xCr steels. Mater Des 186:108307. https://doi.org/10.1016/j.matdes.2019.108307
14 Yang Y, Zhang J, Hu C et al (2019) Structures and properties of Fe-(8-16)Mn-9Al-0.8C low density steel made by a centrifugal casting in near-rapid solidification. Mat Sci Eng A 748:74-84
15 Xu Z, Dai Y, Fang Y et al (2018) High-temperature phase transition behavior and magnetocaloric effect in a sub-rapidly solidified La-Fe-Si plate produced by centrifugal casting. J Mater Sci Technol 34:1337-1343
16 Flemings MC (1990) Solidification processing at near-rapid and rapid rates. In: Weinberg F (ed) International symposium on solidification processing, pp 173-194
17 Xing C, Etemadi R, Pillai KM et al (2022) Numerical simulation on thermal stresses and solidification microstructure for making fiber-reinforced aluminum matrix composites. Materials 15(12):4166. https://doi.org/10.3390/ma15124166
18 Launder BE, Spalding DB (1974) The numerical computation of turbulent flows. Comput Methods Appl Mech Eng 3:21. https://doi.org/10.1016/B978-0-08-030937-8.50016-7
19 Shibuya K, Ozawa M (1991) Strip casting techniques for steel. ISIJ Int 31(7):661-668
20 Liu L, Li C, Yang Y et al (2017) A simple method to produce austenite-based low-density Fe-20Mn-9Al-0.75C steel by a near-rapid solidification process. Mat Sci Eng A 679:282-291
21 Flemings MC (1974) Solidification processing. Metall Mater Trans B 5:2121-2134
22 Fukui Y (1991) Fundamental investigation of functionally gradient material manufacturing system using centrifugal force. JSME Int J 34:144-148
23 Wu SP, Li CY, Guo JJ et al (2006) Numerical simulation and experimental investigation of two filling methods in vertical centrifugal casting. T Nonferr Met Soc 16:1035-1040
24 Azevedo CRF, Maia RR, Ariza EA et al (2014) Failure analysis of a martensitic stainless steel (CA-15M) roll manufactured by centrifugal casting. Part I: material and fractographic characterization. Eng Fail Anal 36:343-352
25 Feng X, Qiu J, Ma Y et al (2016) Influence of processing conditions on microstructure and mechanical properties of large thin-wall centrifugal Ti-6Al-4V casting. J Mater Sci Technol 32:362-371
26 Saluja R, Moeed KM (2012) The emphasis of phase transformations and alloying constituents on hot cracking susceptibility of type 304L and 316L stainless steel welds. J Eng Sci Technol 4:2206-2216
27 Chiang PJ, Jiang R, Cunningham R et al (2019) In situ characterization of hot cracking using dynamic X-ray radiography. The minerals, metals and materials series. Springer, Cham, pp 77-85. https://doi.org/10.1007/978-3-030-06143-2_8
28 Chen K, Huang B, Wang Q et al (2020) Structure and toughness modulation of a Zr52.5Cu17.9Ni14.6Al10Ti5 metallic glass by surface mechanical attrition treatment. J Theor Appl Mech 52:400-407